CdmHub will be intermittently unavailable due to scheduled maintenance the afternoon of Thursday, July 9, 2020. The maintenance work will end all tool sessions and there will be some downtime of other features during the maintenance period. Please plan accordingly and we do apologize for any inconvenience. close

We are using VABS to model section properties of composite circular section beams (golf shafts).

We noticed some counter intuitive results in the following situation. Your advice would be more than welcome.

As you could see in the attached file we are modeling one multi layer section with one orthotropic material (unidirectional UD carbon fiber prepreg).

The case 1 is the base-line laminate made of 32 plies with orientations at 0,+45 and -45 layers.

In case 2 we have the same 32 layers but the orientations of the 6 inner most layers were changed to 90 (hoop direction). Inner and outer diameters remain the same.

We were expecting the section bending stiffness (first term of the Timoshenko stiffness matrix) to decrease from case 1 to case 2. But it increased.

I created case 3 and 4 with even more 90° plies in the inside of the tube. The bending stiffness decreases.

In case 5 the first 6 plies are at +-45°. As expected, the bending stiffness decreases.

Could you please let me know if you see some modeling problems in the files or if you can explain such behavior.

The attached is actually a zip file. Change the extention to .zip to open it. Inside the zip you will find all the related .dat files and an Excel spreadsheet summarizing the results.

Two other things I would like you to try before we know how to advice you: 1) compute the results at the shear center. 2) compare the flexibility matrix at the shear center.

Are all layers of equal thickness ? If so can you provide the thickness of each layers ? And could you provide the radius of the central reference line ?

Could you find attached a new version of the spreadsheet. In this version you could see the inner and outer diameter of the tube as well as the thickness of each layer.

The flexibility matrices are in the dat.K file I sent in my first message. The attached .txt file is actually a zip file. Change the extension to be able to unzip it (for some reason this forum does not accept zip file as attachement)

I wanted to clarify that you are interested in the anomaly which presents itself in "EA" which is the axial stiffness of the cross-section and not "EI" which is the bending stiffness of the cross-section.

In the post you have mentioned that its the bending stiffness and the excel file it is the axial stiffness which you have highlighted.

You are right, I made a confusion in my spreadsheet. We are interested in the bending stiffness of the section and we are getting it from the term 44 of the classical stiffness matrix. Updated spreadseet attached.

According to the VABS documentation, EI2 EI3 are the terms 33 and 44 of the diagonalized stiffness matrix for isotropic materials. Our material is not isotropic. As the non diagonal terms are quite low I do not diagonalize the matrix. I do not really know how bad are these assumptions.

Would you have a more formal method to extract the EI from VABS results for non isotropic section?

However it does not change the problem as we notice the drop in stiffness (calculated by Gebt through natural frequency) when we introduce hoop fibers. This last points illustrates that the section with hoop fiber "stiffer" in bending than the section without. Which is counter intuitive.

For the case of laminated circular tubes Prof. Yu and I have developed an analytical form of the beam stiffness matrix using the basic principles of VABS. I have attached a pdf of the formulas obtained.

These formulas use the values obtained by representing the laminated section in the form of plate and getting its corresponding plate stiffness matrices. In the formulas "Aij, Bij and Dij" represent the corresponding plate stiffness values.

I have attached an excel file which shows results obtained from the formulas for the different cases you have put up and the results are close, though not exact because of the thin-walled assumptions used. These formulas do provide a useful insight to the anomaly which has presented itself.

It can be seen that the axial stiffness does indeed increase as we go from case one to case two, which can be attributed to hoop direction stiffness as well as the Poisson's ratio increasing because of the unique layup configuration. This can also be extended to the case of 33 value, with the increase in the effective Young's modulus of the section in the form of "EA", we can say that "EI" will also show the same trend.

A sensitivity analysis can be conducted using the formulas but coming to a conclusion for the 33 value from the formula itself is difficult as the value depends on a number of quantities as shown.

I hope this clarifies your doubt and I look forward to your views on it.

I understand the stiffness could be increased by the addition of 90° plies (less ovalisation under load...) but I am surprised VABS could capture this phenomenum explicaitaly in the stiffness matrixces without non linear approach.

Could you confirm it does. I would not want to use an artifact to make our design.

Thomas, I believe this is not a nonlinear effect. It is purely due to interaction of the complex 3D stress state which produces an effect counter-intuitive to our intuition obtained from isotropic homogeneous reasoning.

Thanks for your explanation. This is now clear this counter intuitive effect is not an artifact of the model and is captured by VABS for non isotropic material.

It's great such behavior could be seen at section level.

It's very nice to be able to capture these effects without the need for a complete shell model.

Thomas Ricard@ on — Edited @ @ onAll,

We are using VABS to model section properties of composite circular section beams (golf shafts).

We noticed some counter intuitive results in the following situation. Your advice would be more than welcome.

As you could see in the attached file we are modeling one multi layer section with one orthotropic material (unidirectional UD carbon fiber prepreg).

The case 1 is the base-line laminate made of 32 plies with orientations at 0,+45 and -45 layers.

In case 2 we have the same 32 layers but the orientations of the 6 inner most layers were changed to 90 (hoop direction). Inner and outer diameters remain the same.

We were expecting the section bending stiffness (first term of the Timoshenko stiffness matrix) to decrease from case 1 to case 2. But it increased.

I created case 3 and 4 with even more 90° plies in the inside of the tube. The bending stiffness decreases.

In case 5 the first 6 plies are at +-45°. As expected, the bending stiffness decreases.

Could you please let me know if you see some modeling problems in the files or if you can explain such behavior.

The attached is actually a zip file. Change the extention to .zip to open it. Inside the zip you will find all the related .dat files and an Excel spreadsheet summarizing the results.

Thanks in advance for your advice

Best regards

Thomas

TestHoop.txt

595 KBClick to download

Reply Report abuse

Anonymous@ onTwo other things I would like you to try before we know how to advice you: 1) compute the results at the shear center. 2) compare the flexibility matrix at the shear center.

Reply Report abuse

Thomas Ricard@ onHello,

As the section are circular the shaer centers are at 0,0 as you can see in the attached .dat.k files.

does it answer your question?

Best

Thomas

datKFiles.txt

6 KBClick to download

Report abuse

Ankit Deo@ onHello,

Are all layers of equal thickness ? If so can you provide the thickness of each layers ? And could you provide the radius of the central reference line ?

Best Regards,

Ankit

Reply Report abuse

Thomas Ricard@ onHello.

Could you find attached a new version of the spreadsheet. In this version you could see the inner and outer diameter of the tube as well as the thickness of each layer.

Thanks in advance for your help.

Best

Thomas

TestHoop-v2.xlsx

353 KBClick to download

Report abuse

Anonymous@ onPlease also provide corresponding comparison of the flexibility matrix.

Reply Report abuse

Thomas Ricard@ onThe flexibility matrices are in the dat.K file I sent in my first message. The attached .txt file is actually a zip file. Change the extension to be able to unzip it (for some reason this forum does not accept zip file as attachement)

Let me know if it's not what you meant.

Best

Thomas

Report abuse

Ankit Deo@ onHello,

I wanted to clarify that you are interested in the anomaly which presents itself in "EA" which is the axial stiffness of the cross-section and not "EI" which is the bending stiffness of the cross-section.

In the post you have mentioned that its the bending stiffness and the excel file it is the axial stiffness which you have highlighted.

Best Regards,

Ankit

Reply Report abuse

Thomas Ricard@ onAnkit,

You are right, I made a confusion in my spreadsheet. We are interested in the bending stiffness of the section and we are getting it from the term 44 of the classical stiffness matrix. Updated spreadseet attached.

According to the VABS documentation, EI2 EI3 are the terms 33 and 44 of the diagonalized stiffness matrix for isotropic materials. Our material is not isotropic. As the non diagonal terms are quite low I do not diagonalize the matrix. I do not really know how bad are these assumptions.

Would you have a more formal method to extract the EI from VABS results for non isotropic section?

However it does not change the problem as we notice the drop in stiffness (calculated by Gebt through natural frequency) when we introduce hoop fibers. This last points illustrates that the section with hoop fiber "stiffer" in bending than the section without. Which is counter intuitive.

I look forward to continuing this investigation.

Best

Thomas

TestHoop-v3.xlsx

223 KBClick to download

Report abuse

Ankit Deo@ onThomas,

For the case of laminated circular tubes Prof. Yu and I have developed an analytical form of the beam stiffness matrix using the basic principles of VABS. I have attached a pdf of the formulas obtained.

These formulas use the values obtained by representing the laminated section in the form of plate and getting its corresponding plate stiffness matrices. In the formulas "Aij, Bij and Dij" represent the corresponding plate stiffness values.

I have attached an excel file which shows results obtained from the formulas for the different cases you have put up and the results are close, though not exact because of the thin-walled assumptions used. These formulas do provide a useful insight to the anomaly which has presented itself.

It can be seen that the axial stiffness does indeed increase as we go from case one to case two, which can be attributed to hoop direction stiffness as well as the Poisson's ratio increasing because of the unique layup configuration. This can also be extended to the case of 33 value, with the increase in the effective Young's modulus of the section in the form of "EA", we can say that "EI" will also show the same trend.

A sensitivity analysis can be conducted using the formulas but coming to a conclusion for the 33 value from the formula itself is difficult as the value depends on a number of quantities as shown.

I hope this clarifies your doubt and I look forward to your views on it.

Best Regards,

Ankit

TestHoop-TW-VABS.xlsx

9 KBClick to download

Reply Report abuse

Thomas Ricard@ onThanks for these explanation.

I understand the stiffness could be increased by the addition of 90° plies (less ovalisation under load...) but I am surprised VABS could capture this phenomenum explicaitaly in the stiffness matrixces without non linear approach.

Could you confirm it does. I would not want to use an artifact to make our design.

Thanks for your help.

Best regards

Report abuse

Wenbin Yu@ onThomas, I believe this is not a nonlinear effect. It is purely due to interaction of the complex 3D stress state which produces an effect counter-intuitive to our intuition obtained from isotropic homogeneous reasoning.

Cancel Report abuse

Thomas Ricard@ onDear Prof Yu,

Thanks for your explanation. This is now clear this counter intuitive effect is not an artifact of the model and is captured by VABS for non isotropic material.

It's great such behavior could be seen at section level.

It's very nice to be able to capture these effects without the need for a complete shell model.

Thanks for your valuable help.

Best regards

Thomas